Título

Metastability of Mechanically Alloyed and Spark Plasma Sintered Co50soTi50 Powder

Autor

ROBERTO MARTINEZ SANCHEZ

Colaborador

FRANCISCO ESPINOSA MAGAÑA (Colaborador)

JOSE ALBERTO DUARTE MOLLER (Colaborador)

JOSE GERARDO CABAÑAS MORENO (Colaborador)

DAVID RIOS JARA (Colaborador)

Sebastian Diaz de la Torre (Colaborador)

Nivel de Acceso

Acceso Abierto

Licencia

http://creativecommons.org/about/cc0/

Materias

Mechanical Alloying - (PLASMA) Sintering - (CO) Ti - (INTERMETALLIC) CIENCIAS FÍSICO MATEMÁTICAS Y CIENCIAS DE LA TIERRA - (CTI) FÍSICA - (CTI) OTRAS ESPECIALIDADES FÍSICAS - (CTI) OTRAS - (CTI)

Resumen o descripción

High purity cobalt titanium were equiatomically mixed and mechanically alloyed.

The microstructure and phase transformation occurred on the powder product during its

densification using the spark plasma sintering SPS technique were analyzed. CoTi and

CoTi2 intermetallic compounds formed after fast sintering. Although metastable CoTi2

undergoes partial CoTi transformation the lattice parameter and micro-Vickers hardness

of these sintered compounds show high stability when annealing from 973 to 1273 K.

The material thus prepared can be reliably used at these temperatures showing

excellent mechanical behavior.

Fecha de publicación

2000

Tipo de publicación

Artículo

Versión de la publicación

Versión enviada

Recurso de información

http://cimav.repositorioinstitucional.mx/jspui/handle/1004/958

Formato

application/pdf

Idioma

Inglés

Repositorio Orígen

Fuente de Objetos Científicos Open Access

Descargas

364