Título

Extracto acuoso natural de Morinda Citrifolia como inhibidor de corrosión del acero AISI-1045 en ambientes ácidos de HCl.

Autor

Mara Isabel Franco Tronco

Héctor Herrera Hernández

Ivan Garcia Orozco

Pilar Herrasti Gonzalez

Nivel de Acceso

Acceso Abierto

Licencia

http://creativecommons.org/licenses/by-nc-nd/4.0

Materias

Adsorción - ([0034-8570]) AISI 1045 - ([0034-8570]) Corrosión - ([0034-8570]) Extractos - ([0034-8570]) Inhibidor - ([0034-8570]) Morinda Citrifolia - ([0034-8570]) BIOLOGÍA Y QUÍMICA - (CTI)

Resumen o descripción

Mara Franco quisiera agradecer a la beca del CONACYT que le ha permitido realizar su trabajo de tesis y su visita a la Universidad Autónoma de Madrid, UAM. También se agradece al proyecto MAT2015-67557-C2-2-P del Ministerio de Economía y Competitividad por su financiación. En particular el Dr. Héctor Herrera Hernández agradece el apoyo económico recibido por el proyecto de investigación 3817/2014/CID (UAEM-Secretaria de Investigación y Estudios Avanzados). Por último, Dr. Héctor Herrera Hernández y el Dr. Iván García Orozco, reconocen al CONACyT por la distinción al mérito como INVESTIGADOR NACIONAL, SNI.

Natural liquid-extract of Morinda Citrifolia as corrosion inhibitor for steels (AISI-1045) exposed to acidic environments of HCl. Both the organic and inorganic compounds commonly used in the industry to inhibit the corrosion process of metals and its alloys are mostly composed by highly toxic chemicals, in addition to being more expensive. In this research sugar-components derived from the Morinda Citrifolia (MC) leaves have been extracted in aqueous solution to perform a natural inhibitor capable to control de corrosion damage, which can replace the traditional inhibitors, being environmentally friendly. The experimental results indicate that this compound has shown excellent performance as corrosion inhibitor, reaching inhibition efficiency (EI), values up to 90% at inhibitor concentrations ranging 0.8 to 2 g•L−1 and immersion times of about 1 to 4 h. It has been found that the inhibition process takes place by the adsorption of the molecules on the surface of the metal (AISI 1045), by a physisorption mechanism.

proyecto de investigación 3817/2014/CID (UAEM-Secretaria de Investigación y Estudios Avanzados).

Editor

Revista de Metalurgia

Fecha de publicación

1 de octubre de 2018

Tipo de publicación

Artículo

Recurso de información

http://hdl.handle.net/20.500.11799/99377

Fuente

0034-8570

Idioma

Inglés

Relación

54;4

Audiencia

Estudiantes

Investigadores

Repositorio Orígen

REPOSITORIO INSTITUCIONAL DE LA UAEM

Descargas

283