Bioanode of polyurethane graphite polypyrrole composite in microbial fuel cells
Autor
PEDRO PÉREZ RODRÍGUEZ
VÍCTOR MANUEL OVANDO MEDINA
SILVIA YUDITH MARTINEZ AMADOR
JOSE ANTONIO RODRIGUEZ DE LA GARZA
Nivel de Acceso
Acceso Abierto
Materias
Resumen o descripción
"Polyurethane (PU) foams were coated with graphite, and pyrrole monomer was subsequently polymerized onto its surface by chemical oxidization to obtain nanostructured polyurethane/graphite/polypyrrole (PU/Graph/PPy) composites, which were used for anaerobic microorganisms grown and tested as anodes in microbial fuel cells (MFC) using municipal wastewater as fuel. The effects of oxidizing agent type (ammonium persulfate and FeClz) used in pyrrole polymerization on the performance of electrodes in MFC were studied. Composites were characterized by Fourier Transform Infrared (FTIR) spectroscopy, Scanning Electron Microscopy (SEM), and by the four-point probes to determine conductivity. It was observed from SEM analysis that globular nanostructures of PPy were formed onto PU surface with average diameters between 120 and 450 nm, which are typical of aqueous polymerization of pyrrole monomer. The highest output power density observed in MFCs was 305.5 mW/m3 for the composite synthesized using FeCl3 as the oxidant, and 128.6 mW/m3 using the composite obtained with ammonium persulfate as oxidizing; the corresponding chemical oxygen demand (COD) removal were 48.2 and 45.5%, respectively. The calculated coulombic efficiency for PU/Graph/PPy composite obtained with FeCl3 as oxidant was of 9.4%. Internal resistance of MFC using the composite obtained with FeCl3 as-oxidant was determined by linear sweep voltammetry (LSV) and the variable resistance (VR) methods, giving 4.8 and 2.9 KO), respectively, with average maximum power density of 237.5 mW/m3."
Fecha de publicación
2017 2017
Tipo de publicación
Artículo
Versión de la publicación
Versión publicada
Recurso de información
Formato
application/pdf
Idioma
Inglés
Audiencia
Estudiantes
Investigadores
Repositorio Orígen
Repositorio Digital CID-UAAAN
Descargas
0