Ajustar las condiciones de operación de una prensa hidráulica horizontal de fabricación propia para un proceso de doblado en frío a 90°

Hugo Estrada Pimentel HUGO ARCOS GUTIERREZ JOSE ANTONIO BETANCOURT CANTERA Jan Mayén Chaires John Edison García Herrera (2023)

During the cold-bending process, the tooling suffers considerable damage due to excess pressure. This also causes the machines to break down, causing problems in the precision and quality of the metal parts formed. The precision depends on the operating conditions of the press, the tooling employed, and the elastic recovery effect of the material. This study determines the working conditions for a made-in-house horizontal hydraulic press through an experimental design (DOE). This research carried out the V-forming to 90° (ISO 2768-1) of a hot-rolled carbon steel plate, considering pressure, piston permanence time, and recovery factor (Kr). The experimental and statistical analysis ensures accurate forming while the work pressure decreases by 17% and 33%, respectively, regarding the maximum. This reduction will delay the appearance of fatigue damage and have the operating parameters well established; in turn, it will be possible to design tools according to commercial standards.

Durante el proceso de conformado en frío, las herramientas sufren daños considerables debido al exceso de presión. Esto también causa que las máquinas se rompan, causando problemas en la precisión y calidad de las piezas metálicas formadas. La precisión depende de las condiciones de funcionamiento de la prensa, las herramientas empleadas y el efecto elástico de recuperación del material. Este estudio determina las condiciones de trabajo de una prensa hidráulica horizontal fabricado en casa a través de un diseño experimental (DOE). Esta investigación llevó a cabo el conformado en V a 90° (ISO 2768-1) de una placa de acero al carbono laminada en caliente, teniendo en cuenta la presión, el tiempo de permanencia del pistón y el factor de recuperación (Kr). El análisis experimental y estadístico asegura un conformado preciso, mientras que la presión de trabajo disminuyó en un 17% y 33%, respectivamente, con respecto al máximo. Esta reducción retrasará la aparición de daños por fatiga y tendrá los parámetros de funcionamiento bien establecidos; con estos, a su vez, será posible diseñar herramientas de acuerdo con los estándares comerciales.

Authorship acknowledgement: Hugo Estrada: Conceptualization; methodology; validation; writing; revision; project administration; software; investigation; display; draft writing; reviewing and editing. Hugo Arcos: Conceptualization; methodology; validation; writing; revision; simulation; software; reviewing. José A. Betancourt: Supervision; methodology; validation; writing; revision; draft writing: writing reviewing and editing. Jan Mayen: Supervision; methodology; validation; writing; revision; formal analysis.

John E. García: Conceptualization; supervision; methodology; validation; writing; revision; project management; formal analysis, draft writing: writing reviewing and editing.

Artículo

Cold forming DOE ANOVA Recovery factor (Kr) Factorial analysis 2k Spring back (SB) Conformado en frío Factor de recuperación (Kr) Análisis factorial 2k Recuperación elástica (SB) INGENIERÍA Y TECNOLOGÍA CIENCIAS TECNOLÓGICAS OTRAS ESPECIALIDADES TECNOLÓGICAS OTRAS OTRAS

Effect of the noble metals addition on the oxidation behavior of Ni3Al

Jose Juan Ramos-Hernandez JESUS PORCAYO-CALDERON Jan Mayen Chaires GABRIEL ANGEL LARA RODRIGUEZ victor salinas JOSE-GONZALO GONZALEZ-RODRIGUEZ Lorenzo Martínez Gómez (2018)

This paper discusses the e1ect of the addition of noble metals on the microstructure, mechanism, and oxidation kinetics of the Ni3Al intermetallic alloy. Ni3Al was doped with 1% (atomic percent) of Au, Ag, Pd, and Pt. Oxidation behavior of the alloys was evaluated at 900, 1000, and 1100°C in O2 for 24 hours. XRD analysis showed that the addition of noble metals favored the oxide growth on preferential crystallographic planes. In addition, the preferential substitution of the noble metals in the Ni3Al structure modi>es the surface composition by increasing the Al/Ni ratio. It was observed that most of the alloys showed a subparabolic behavior, and only the intermetallic base and the alloy doped with Ag show a parabolic behavior at 900°C. ,e developed oxides were analyzed both super>cially and in cross section by scanning electron microscopy (SEM) and energy dispersive X-ray analysis (EDXA). It was evident that only the intermetallic base showed the formation of a duplex oxide scale (Al2O3/NiO). ,e alloys doped with noble metals showed the oxide growth practically of pure Al2O3. ,is was due to a decrease in the di1usion of the Ni cations because of the presence of the noble metals in the crystalline structure.

Financial support from Consejo Nacional de Ciencia y Tecnologia (CONACYT, Mexico) (Project no. 159898 and Ph.D. scholarship to J. J. Ramos-Hernandez, Registration no. 202898) is gratefully acknowledged.

Artículo

INGENIERÍA Y TECNOLOGÍA CIENCIAS TECNOLÓGICAS TECNOLOGÍA DE MATERIALES PROPIEDADES DE LOS MATERIALES PROPIEDADES DE LOS MATERIALES