Synthesis of Ferroelectric and Multiferroics Thin films of BiMnO3/ SrTiO3 and Structural, Piezoelectric, Magnetic, Optical, and Mechanical Properties Characterization

Glory Valentine Umoh (2022, [Tesis de doctorado])

Multiferroic characteristics of BiMnO3 thin films offer great prospects to explore, either

in terms of ferroelectricity, ferromagnetism, or ferroelasticity. Ferroelectric and

ferromagnetic materials can be used in data storage due to their electrical and magnetic

properties. Ferroelastic can find its application in microelectromechanical systems

devices. This dissertation focused on the synthesis, characterization, and improvement of

the multiferroic properties of polycrystalline BiMnO3 thin films as well as the elaboration

influence of Cu on the magnetism of BiMnO3 thin films. BiMnO3 films were grown on

three different substrates, Si (001), Pt-buffered Si (001), Nb-doped SrTiO3 (100), and also

doped with different amounts of Cu. The films were characterized using techniques such

as X-Ray diffraction (XRD), scanning electron microscope (SEM), HRTEM

observations, by energy-dispersive X-ray spectroscopy (EDS), atomic force microscopy

(AFM), X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, Visible-near-IR

spectroscopy (Vis-NIR), electron energy loss spectrometer (EELS), nanoindenter,

superconductor quantum interference device (SQUID) magnetometer, and finally, the

polarization-electric field (P-E) hysteresis loops of the BiMnO3 thin films were conducted

at 200 and 300 K. There are several studies on the growth of thin films, however, they are

not clear and in some cases contradictory, therefore, different parameters were controlled

during the deposition in terms of working pressure, RF power, substrate, deposition

10

temperature, and target to substrate distance. After deposition ex-situ thermal treatment

was carried out in order to compensate for the volatility of bismuth and also to eliminate

secondary phase.

Kramer’s–Krӧnig analysis was used to determine bandgap, via a polynomial fit in the

energy loss function (ELF) plot with an Eg = 1.63 eV, complex dielectric function, and

static dielectric constant, ε* = 4.68 of the grown BiMnO3 thin films. The reflection

coefficient Ґl of the BiMnO3 thin films was used to elucidate the reflection loss in the

BiMnO3 thin films. XPS analysis revealed the existence of Mn charge transition of 3+

and 4+ states. Resistivity result describes BIMnO3 as a semiconductor. The

nanomechanical characterization demonstrated that the region of penetration depth was

below 10% of BiMnO3 film thickness. Young's modulus (E), hardness (H), and Stiffness

(S) were measured to be 142 ± 3 GPa, 8 ± 0.2 GPa, and 44072 ± 45 N/m respec

SÍNTESIS DE MATERIALES Materiales Multiferroicos CIENCIAS FÍSICO MATEMÁTICAS Y CIENCIAS DE LA TIERRA FÍSICA OTRAS ESPECIALIDADES FÍSICAS OTRAS OTRAS

Fabricación de nanopartículas de oro dentro de óxido de aluminio (γ-Al2O3) nanoestructurado con cavidades esféricas

Manufacturing of Gold Nanoparticles within Nanostructured Aluminum Oxide (γ-Al2O3) with Spherical Cavities

Mariela de Jesús Franco Gallegos (2023, [Tesis de maestría])

Los catalizadores basados en nanopartículas de oro han generado gran interés, gracias a su capacidad de ser selectivos en la promoción de reacciones específicas o en la producción de productos deseados, minimizando la formación de productos secundarios no deseados; sus propiedades electrónicas únicas; y su utilización bajo condiciones ambientales. Sin embargo, la desventaja principal de los catalizadores de oro es la sinterización de las nanopartículas debido a su baja temperatura de fusión, lo que provoca la pérdida de actividad catalítica y la desactivación del catalizador. Una de lassoluciones que ofrece el uso de la nanociencia y la nanotecnología es la utilización de soportes nanoestructurados que den mejor estabilidad a las nanopartículas y las protejan de la desactivación. En este trabajo se sintetizaron catalizadores basados en nanopartículas de oro soportados y encapsulados en alúmina macroporosa, por un método de impregnación húmeda asistida por ultrasonido; un método sencillo, rápido y ecológico. El desempeño catalítico de materiales sintetizados se analizó mediante espectroscopía UV-Visible in-situ en la reducción de 4-Nitrofenol a 4-Aminofenol. Así mismo, se presentan las caracterizaciones por TEM, SEM, FT-IR, espectroscopía UV-Visible, y XRD de catalizadores obtenidos. Se obtuvieron catalizadores altamente activos con alto rendimiento gracias al uso de un soporte nanoestructurado.

Catalysts -based on gold nanoparticles have recently gained interest due to their ability to selectively promote specific catalytic reactions or produce desired products, while minimizing the formation of unwanted byproducts, their unique electronic properties, and their utilization under ambient conditions. However, the main drawback of gold catalysts is the sintering of nanoparticles due to their low melting temperature, which leads to loss of catalytic activity and catalyst deactivation. One of the solutions offered by nanoscience and nanotechnology is the use of nanostructured supports that provide better stability to the nanoparticles and protect them from deactivation. In this work, gold nanoparticle-based catalysts supported and encapsulated in macroporous alumina were synthesized using a simple, fast, and eco-friendly method of ultrasound-assisted wet impregnation. The catalytic performance of synthetized materials was evaluated by in-situ UV-Visible spectroscopy in the reduction of 4-Nitrophenol to 4-Aminophenol. In addition, their characterization by TEM, SEM, FT-IR, UV Visible spectroscopy and XRD are presented. Highly active catalysts with high performance were obtained thanks to the use of a nanostructured supports.

nanopartículas de oro, alúmina macroporosa, impregnación, reducción 4-NF gold nanoparticles, macroporous alumina, impregnation, 4-NF reduction INGENIERÍA Y TECNOLOGÍA CIENCIAS TECNOLÓGICAS TECNOLOGÍA DE MATERIALES PROPIEDADES DE LOS MATERIALES PROPIEDADES DE LOS MATERIALES

Tensile behavior of 3D printed polylactic acid (PLA) based composites reinforced with natural fiber

Eliana M Agaliotis BALTAZAR DAVID AKE CONCHA ALEJANDRO MAY PAT Juan Pablo Morales Arias Celina Bernal Alex Valadez González Pedro Jesús Herrera Franco Gwenaelle Proust JUAN FRANCISCO KOH DZUL José Gonzalo Carrillo Baeza Emmanuel Alejandro Flores Johnson (2022, [Artículo])

Natural fiber-reinforced composite (NFRC) filaments for 3D printing were fabricated using polylactic acid (PLA) reinforced with 1–5 wt% henequen flour comprising particles with sizes between 90–250 μm. The flour was obtained from natural henequen fibers. NFRCs and pristine PLA specimens were printed with a 0° raster angle for tension tests. The results showed that the NFRCs’ measured density, porosity, and degree of crystallinity increased with flour content. The tensile tests showed that the NFRC Young’s modulus was lower than that of the printed pristine PLA. For 1 wt% flour content, the NFRCs’ maximum stress and strain to failure were higher than those of the printed PLA, which was attributed to the henequen fibers acting as reinforcement and delaying crack growth. However, for 2 wt% and higher flour contents, the NFRCs’ maximum stress was lower than that of the printed PLA. Microscopic characterization after testing showed an increase in voids and defects, with the increase in flour content attributed to particle agglomeration. For 1 wt% flour content, the NFRCs were also printed with raster angles of ±45° and 90° for comparison; the highest tensile properties were obtained with a 0° raster angle. Finally, adding 3 wt% content of maleic anhydride to the NFRC with 1 wt% flour content slightly increased the maximum stress. The results presented herein warrant further research to fully understand the mechanical properties of printed NFRCs made of PLA reinforced with natural henequen fibers. © 2022 by the authors.

POLYLACTIC ACID (PLA) NATURAL FIBER HENEQUEN FIBER NATURAL FIBER REINFORCED COMPOSITE (NFRC) ADDITIVE MANUFACTURING 3D PRINTING MECHANICAL PROPERTY INGENIERÍA Y TECNOLOGÍA CIENCIAS TECNOLÓGICAS TECNOLOGÍA DE MATERIALES PROPIEDADES DE LOS MATERIALES PROPIEDADES DE LOS MATERIALES

First-principles calculations focused on the study of MXenes with potential applications in energy storage devices

First-principles calculations focused on the study of MXenes with potential applications in energy storage devices

Victor Hugo Medina Macias (2023, [Tesis de maestría])

First-principles studies of Ti/Ta-based ordered alloy MXenes have demonstrated their viability as anode material in Li-ion batteries due to their promising electrochemical properties. However, the influence of surface functional groups on the atomic-scale lithiation processes remains unknown. In this thesis, we employ first-principles density functional theory (DFT) calculations to investigate the thermodynamic stability, structural characteristics, and electrochemical properties of O-, F-, Cl-, and OH-functionalized Ti2Ta2C3 ordered alloy MXenes during Li intercalation. Our calculations reveal surface functionalization with O, F, Cl, and OH is thermodynamically stable, indicating their viability as functional groups. Also, we identify the H3 high symmetry site as the most favorable configuration for Li intercalation. To evaluate electrochemical performance, electrochemical characterization is carried out employing open circuit voltage (OCV) curves. Our findings demonstrate changes in storage capacities depending on the functional group, with O-functionalized MXenes exhibiting larger storage capacities in contrast to other functional groups in Ti2Ta2C3 MXene anode materials. The theoretical single-layer gravimetric storage capacities for O-, F-, and Cl-functionalized Ti2Ta2C3 MXene anodes are 91.77, 52.38, and 24.21 mAh/g, respectively. OH-functionalized MXenes failed to show thermodynamic stability during lithiation and favored Li cluster formation over an intercalation process. These results show how functional groups affect the potential performance of Ti2Ta2C3 MXene materials in energy storage applications and provide insights for correctly selecting the functional group of the host material.

Mediante cálculos de primeros principios se ha demostrado la viabilidad del MXene formado por la aleación ordenada Ti/Ta como material anódico en baterias de iones de litio, esto debido a sus propiedades electroquímicas prometedoras. Sin embargo, la influencia de los grupos funcionales superficiales en el proceso atómico de litiación permanecen desconocidos. En esta tésis, empleamos cálculos de primeros principios basados en la Teoría del Functional de la Densidad (DFT) para investigar la estabilidad termodinámica, las características estructurales y las propiedades electroquímicas del MXene de aleación ordenada Ti2Ta2C3 funcionalizado con grupos O, F, Cl y OH, durante el proceso de intercalación de iones de litio. Nuestros cálculos demuestran la estabilidad termodinámica de la funcionalización superficial con grupos O, F, Cl y OH, indicando su viabilidad como grupos funcionales. Adicionalmente, identificamos el sitio de alta simetría H3 como la configuración más estable para la intercalación de Li. Para evaluar el rendimiento electroquímico, se realizó la caracterización electroquímica empleando curvas de voltage de circuito abierto (OCV). Nuestros hallazgos demuestran cambios en la capacidad de almacenamiento dependiendo del grupo funcional, siendo el MXene funcionalizado con oxígenos el que exhibe mayores capacidades de almacenamiento en contrastre con los otros grupos funcionales presentes en el MXene Ti2Ta2C3. Las capacidades gravimétricas de almacenamiento para los ánodos de Ti2Ta2C3 de una sola capa funcionalizados con O, F y Cl son 91.77, 52.38 y 24.21 mAh/g, respectivamente. Los MXenes funzionalizados con grupos OH no mostraron estabilidad termodinámica durante el proceso de litiación y favorecieron la formación de clusters de Li en su lugar. Estos resultados demuestran cómo los grupos funcionales cambian el rendimiento potencial de MXenes de Ti2Ta2C3 en aplicaciones de almacenamiento de energía y proporciona información para seleccionar correctamente el grupo funcional del material base.

MXene, MXene de aleación ordenada, Bateria de Li-ion, Material anódico MXene, ordered alloy MXene, Li-ion battery, Anode material INGENIERÍA Y TECNOLOGÍA CIENCIAS TECNOLÓGICAS TECNOLOGÍA DE MATERIALES PROPIEDADES DE LOS MATERIALES PROPIEDADES DE LOS MATERIALES

Preparation and characterization of strongly sulfonated acid block and random copolymer membranes for acetic acid esterification with 2-Propanol

Verónica Rosiles González Ronan Le Lagadec ARELLY PAULINA VARGUEZ CATZIM María Isabel de los Dolores Loría Bastarrachea Abigail Gonzalez Diaz EMANUEL HERNANDEZ NUÑEZ Manuel de Jesús Aguilar Vega MARIA ORTENCIA GONZALEZ DIAZ (2022, [Artículo])

In this paper, we report the synthesis of block and random copolymers of 2-acrylamido-2-methyl-1-propane sulfonic acid (AMPS) and methyl methacrylate (MMA), with different AMPS feed ratios. These solution-processable copolymers with strongly sulfonated acid groups resulted in membranes with tunable ion exchange (IEC) and water absorption capacities. AFM images confirmed the microphase separation of PAMPS-b-PMMA-1:1 block copolymer membrane, annealed under the appropriate conditions. The resulting copolymers from the random combination of a 1:1 molar ratio of AMPS and MMA monomers are effective at enhancing the esterification conversion of acetic acid, when compared with a reaction catalyzed by PAMPS-b-PMMA block copolymers and the previously studied catalytic membranes. With the PAMPS-co-PMMA-1:1 membrane, the esterification reaction using acetic acid achieved 85% isopropyl acetate. These results are closely correlated with the increase in IEC (2.63 mmol H+ g−1 ) and the relationship between weight loss (20.3%) and swelling degree (68%) in 2-propanol. © 2022 by the authors. Licensee MDPI, Basel, Switzerland.

BLOCK COPOLYMERS RANDOM COPOLYMERS CATALYTIC MEMBRANES ESTERIFICATION ISOPROPYL ACETATE INGENIERÍA Y TECNOLOGÍA CIENCIAS TECNOLÓGICAS TECNOLOGÍA DE MATERIALES PROPIEDADES DE LOS MATERIALES PROPIEDADES DE LOS MATERIALES

Thermal and mechanical properties of PLA-based multiscale cellulosic biocomposites

MIGUEL ANGEL RUZ CRUZ Pedro Jesús Herrera Franco Emmanuel Alejandro Flores Johnson MARIA VERONICA MORENO CHULIM LUCIANO MIGUEL GALERA MANZANO Alex Valadez González (2022, [Artículo])

In this work polylactic acid (PLA) based multiscale cellulosic biocomposites were prepared with the aim to evaluate the effect of the incorporation of cellulose nanocrystals (CNCs) on the PLA biocomposites reinforced with cellulose microfibers (MFCs). For this, PLA composite materials reinforced with both MFCs and with a combination of MFCs and CNCs were prepared, while keeping the content of cellulosic reinforcements constant. The thermal and mechanical properties of these multiscale PLA biocomposites were characterized by thermogravimetry (TGA), differential scanning calorimetry (DSC), flexural mechanical and, dynamic mechanical (DMA) tests. Likewise, they were characterized by Fourier transform infrared spectroscopy (FTIR) and scanning electron microscopy (SEM). The results show that the replacement of MFCs by CNCs in the 1–5% range appreciably modifies the thermal and mechanical properties of multiscale compounds. For example, they increase the thermal stability of the materials, modify the PLA crystallization process and play the role of adhesion promoters since the mechanical properties in flexure increase in the order of 40% and the storage modulus increases in the order of 35% at room temperature. Also, the addition of CNCs increases the relaxation temperature of the material from 50 to 60 °C, thereby expanding the temperature range for its use. © 2022 The Author(s)

MULTISCALE BIOCOMPOSITES CELLULOSE MICROFIBER CELLULOSE NANOCRYSTALS HIERARCHICAL STRUCTURE PROPERTIES INGENIERÍA Y TECNOLOGÍA CIENCIAS TECNOLÓGICAS TECNOLOGÍA DE MATERIALES PROPIEDADES DE LOS MATERIALES PROPIEDADES DE LOS MATERIALES

Estudio y caracterización del Sargazo para uso y disposición

David Quiroz Cardoza (2022, [Tesis de maestría])

El masivo arribo de sargazo a las costas es un problema de carácter social,

ambiental y económico. Por tal motivo, el objetivo de este trabajo es evaluar los

productos obtenidos de la digestión anaerobia (DA) del sargazo para su

valorización desde la perspectiva circular para el uso del material no digerido

(Digestato) como mejoradores de suelos.

Bajo las consideraciones teóricas, establecidas por el cálculo del potencial de

metanización (BPM), se establecieron las relaciones C/N 15, 20 y 30 que

favorecían la digestión del sustrato en el desarrollo experimental. Además de

considerar tres tamaños de partícula, 5, 2 y 0.6 mm, para su fermentación. El

tamaño de partícula de 2 mm, mostró mejores resultados experimentales en la

generación de biogás produciendo hasta 1763 cm3

/gSV de biogás y hasta 1401.03

mL de CH4, mientras que la evaluación del potencial bioquímico de metano (PBM)

experimental alcanzo un acumulado de 92.62 mL CH4/gSV en 35 días de

tratamiento. De acuerdo con estos resultados es posible el obtener biogás de la

DA del sargazo con una composición de metano aceptable para su valorización.

La alta concentración del sulfuro de hidrogeno en el biogás, de hasta 15,721.66

mg/L al inicio de la digestión anaerobia, aun cuando disminuye con el tiempo hace

obligatorio el pretratamiento para reducir esta concentración según su aplicación.

El digestato obtenido luego de la DA tiene los nutrientes para ser valorizado como

un mejorador de suelos según la NTEA-006-SMA-2006. Sin embargo, existe la

limitante debido a que sobrepasa los niveles permisibles de metales pesados

como arsénico 5 mg/Kg, encontrando en los digestatos evaluados valores desde

los 19 mg/Kg hasta los 30 mg/Kg de arsénico. Además en las pruebas de

germinación para la partícula de 2 mm se muestran índices que indican una

toxicidad de moderada a baja en concentraciones entre el 60 y 100% de digestato

puro, indicando que el digestato influye en los procesos de germinación.

El cálculo de huella de carbono, concluye que el impacto causado de implementar

o no la DA como tecnología para el aprovechamiento del sargazo de las playas

mexicanas se le atribuye un 66.18% a la recolección y transporte, dejando un

33.82% restante relacionado a la digestión anaerobia.

Caracterización de materiales Sargazo INGENIERÍA Y TECNOLOGÍA CIENCIAS TECNOLÓGICAS INGENIERÍA Y TECNOLOGÍA DEL MEDIO AMBIENTE OTRAS OTRAS

Síntesis de sistema Cturbo/ZnO/CuO con aplicación en degradación de colorante por fotocatálisis

Jose Manuel Riega Medina (2022, [Tesis de maestría])

La contaminación del agua por compuestos orgánicos tóxicos es un problema

que ha sido estudiado y abordado de diferentes formas. Para dar una solución a

esta problemática, se han propuestos diversos métodos y mecanismos de descontaminación.

Dentro de estos, la fotocatálisis heterogénea se presenta como una

solución amigable con el medio ambiente y de bajo costo energético. Por otro lado,

la síntesis de alótropos del carbono con fotocatalizadores, ha demostrado mejorar

la actividad de estos para fotodegradar compuestos orgánicos. Adicionalmente, el

ordenamiento turboestrático del carbono, compuesto de grafeno y grafito exfoliado,

se presenta como un material promisorio ya que tiene propiedades muy parecidas

al grafeno de pocas capas [1].

En la presente tesis se sintetizó el carbono turboestrático (Cturbo) por una variante

del método dry ice. La caracterización por Difracción de Rayos X (DRX) y espectroscopía

Raman, mostró la estructura del carbono y los defectos presentes en la red

grafítica. Con la Microscopía Electrónica de Barrido (MEB) y Microscopía Electrónica

de Transmisión (MET) se observó el apilamiento turboestrático del carbono junto

con planos de grafeno y grafito exfoliado. Las propiedades texturales mostraron que

el Cturbo es un material mesoporoso con un área superficial de 634 m2/g. La prueba

de adsorción del Anaranjado de Metilo (AM) en el Cturbo determinó que el modelo

de Freundlich es el que mejor describe el tipo de adsorción entre estos. El sistema

Cturbo/ZnO/CuO se sintetizó por los métodos de calcinación y coprecipitado. La

caracterización por DRX mostró las tres fases presentes. El área superficial del sistema

aumenta con el aumento de la cantidad de Cturbo presente. En la MEB y MET

se observó las partículas de ZnO y CuO dispersas sobre el Cturbo. El ancho de banda

prohibida del sistema disminuye con el aumento de Cturbo. Las pruebas de fotocatálisis

bajo radiación ultravioleta (UV), mostraron que el Cturbo, en el sistema, aumenta

la degradación del AM en comparación a cuando se realizó la prueba solo con los

óxidos.

Este estudio presenta un nuevo método para sintetizar el ordenamiento turboestrática

del carbono y una posible aplicación de este como sustrato para mejorar las

propiedades fotocatalíticas del ZnO y CuO.

Síntesis de materiales Contaminación CIENCIAS FÍSICO MATEMÁTICAS Y CIENCIAS DE LA TIERRA FÍSICA QUÍMICA FÍSICA OTRAS OTRAS

Análisis a escala atómica de interfases magnéticas con aplicaciones en espintrónica

Atomic scale analysis of magnetic interfases with spintronics applications

Rocio González Díaz (2023, [Tesis de maestría])

La espintrónica es un área de la nanociencia que tiene por cometido el estudio y manipulación del espín de los electrones para el desarrollo y mejoramiento de dispositivos electrónicos. De manera particular, se ha orientado a la búsqueda de materiales para la fabricación de memorias magnéticas de acceso aleatorio (MRAM), diseñadas a partir de uniones túnel magnéticas (MTJ). Dichas uniones son heteroestructuras construidas a partir de un material aislante en cuya capa superior e inferior se dispone un compuesto ferromagnético. Una de las características de estos dispositivos es que presentan una anisotropía magnética perpendicular (PMA) y un efecto de torque por transferencia de espín (STT). Recientemente, un estudio experimental señala que la heteroestructura B2-CoAl/L10-MnAl es un candidato idóneo para la fabricación de MRAM, pues presenta PMA y STT. Sin embargo, en el trabajo experimental no se reporta un análisis de la estabilidad termodinámica de la heteroestructura. Dicho lo anterior, en este trabajo se hizo un estudio de la estabilidad termodinámica y estructural de B2-CoAl/L10-MnAl usando la teoría del funcional de la densidad (DFT). Se propusieron diferentes modelos de interfaz CoAl/MnAl y se determinó a través de un análisis energético cuál es la interfaz más estable. Los resultados obtenidos indican que la interfaz más estable sucede entre la última capa de Al del CoAl y la primera capa de Mn del MnAl. Además, se comprobó un efecto PMA en la heteroestructura B2-CoAl/L10-MnAl y se determinó que este comportamiento se origina esencialmente debido a la naturaleza ferromagnética de MnAl, pues CoAl no presenta características ferromagnéticas.

Spintronics is nanoscience area whose aim is the study and manipulation of electrons spin to development and improvement of electronic devices. In a particular way, the spintronics has focused to search of new materials to fabrication of magnetic random-access memory (MRAM), which are designed from devices call magnetic tunnel junctions (MTJ). This devices are heterostructures built from an insulating material with a ferromagnetic compound on top and bottom layers and characterized by the perpendicular magnetic anisotropy and spin-transfer torque (STT) effects prensent on it. Recently, an experimental study indicates the B2-CoAl/L10-MnAl heterostructure is a suitable candidate for the fabrication of MRAM based on MTJ devices. Nevertheless, the thermodynamic stability of the heteroestructure is not reported in the experimental work. Therefore, in this work a study of the thermodynamic and structural stability of B2-CoAl/L10-MnAl was performed using density functional theory (DFT). Different CoAl/MnAl interface models were proposed and the most stable interface was determined by an energy analysis. The results obtained, indicate that the most stable interface occurs between the last Al layer of CoAl and the first Mn layer of MnAl. In addition, a PMA effect in the B2-CoAl/L10-MnAl heterostructure was demonstrated and it was determined that this behaviour is essentially due to the ferromagnetic nature of MnAl, since CoAl does not present ferromagnetic characteristics.

simulaciones computacionales, interfases magnéticas, estabilidad termodinámica computational simulation, magnetic interfaces, termodinamic stability INGENIERÍA Y TECNOLOGÍA CIENCIAS TECNOLÓGICAS TECNOLOGÍA DE MATERIALES PROPIEDADES DE LOS MATERIALES PROPIEDADES DE LOS MATERIALES

Effect of the noble metals addition on the oxidation behavior of Ni3Al

Jose Juan Ramos-Hernandez JESUS PORCAYO-CALDERON Jan Mayen Chaires GABRIEL ANGEL LARA RODRIGUEZ victor salinas JOSE-GONZALO GONZALEZ-RODRIGUEZ Lorenzo Martínez Gómez (2018, [Artículo])

This paper discusses the e1ect of the addition of noble metals on the microstructure, mechanism, and oxidation kinetics of the Ni3Al intermetallic alloy. Ni3Al was doped with 1% (atomic percent) of Au, Ag, Pd, and Pt. Oxidation behavior of the alloys was evaluated at 900, 1000, and 1100°C in O2 for 24 hours. XRD analysis showed that the addition of noble metals favored the oxide growth on preferential crystallographic planes. In addition, the preferential substitution of the noble metals in the Ni3Al structure modi>es the surface composition by increasing the Al/Ni ratio. It was observed that most of the alloys showed a subparabolic behavior, and only the intermetallic base and the alloy doped with Ag show a parabolic behavior at 900°C. ,e developed oxides were analyzed both super>cially and in cross section by scanning electron microscopy (SEM) and energy dispersive X-ray analysis (EDXA). It was evident that only the intermetallic base showed the formation of a duplex oxide scale (Al2O3/NiO). ,e alloys doped with noble metals showed the oxide growth practically of pure Al2O3. ,is was due to a decrease in the di1usion of the Ni cations because of the presence of the noble metals in the crystalline structure.

Financial support from Consejo Nacional de Ciencia y Tecnologia (CONACYT, Mexico) (Project no. 159898 and Ph.D. scholarship to J. J. Ramos-Hernandez, Registration no. 202898) is gratefully acknowledged.

INGENIERÍA Y TECNOLOGÍA CIENCIAS TECNOLÓGICAS TECNOLOGÍA DE MATERIALES PROPIEDADES DE LOS MATERIALES PROPIEDADES DE LOS MATERIALES